Kif il-Frazzjoni tal-Volum ta 'Carbides MC Primarji (NbC/TiC) minn Nijobju Eċċess (0.60-0.80 wt%) f'347 Heater Sheath Tubing Jikkontrolla d-Densità tas-Sit tal-Inizjazzjoni tal-Pit u l-Ħin ta' Perforazzjoni f'1,000 ppm Ilma tal-Klorur f'80 grad

Servizz ta' Klorur Over-Penali ta' Stabbilizzazzjoni għar-Reżistenza għall-Pitting

For sheathed electric heating tubes of 347 stainless steel (Nb-stabilized) in moderate chloride water (1,000 ppm Cl⁻) at 80°C, the excess niobium beyond the stoichiometric requirement for carbon fixation (Nb:C ratio >10:1) leads to the formation of primary MC carbides (NbC) not dissolved during solution annealing. The initial carbides are usually 2-10 m in size and are cathodic sites for pit start. At 0.30-0.40 wt % niobium (Nb:C = 8:1 to 10:1) principal MC volume percentage is 0.04-0.06% and service life >10 snin. Il-frazzjoni tal-volum MC primarja tiżdied għal 0.12-0.20% (stabbilizzat żżejjed (0.60-0.80 wt% nijobju)) Id-densità tal-fossa tiżdied 5-10 darbiet Il-ħin tal-perforazzjoni jonqos għal 2-4 snin Dan id-dokument jevalwa r-rabta bejn l-eċċess ta 'Nb, primarja MC karbur ta' volum de frazzjoni, bidu tal-frazzjoni tal-volum tal-karbur MC, pp0 bidu tal-perforazzjoni u ppm0 Cl⁻ ilma fi 80 grad.

Il-Mekkaniżmu ta 'Pitting Immexxi mill-Primarja MC Carbide

Matul is-solidifikazzjoni tal-istainless steel 347, il-karburi MC primarji (NbC, TiC) huma ffurmati. Minħabba l-konduttività elettrika għolja tagħhom u l-kwalitajiet tal-wiċċ nobbli huma katodiċi għall-matriċi awstenitika. Jekk il-kontenut tan-nijobju huwa 'l fuq minn madwar 0.45-0.50 wt% (il-kontenut normali tal-karbonju huma 0.04-0.06%) allura kwalunkwe nijobju żejjed lil hinn mill-ammont meħtieġ għall-istabbilizzazzjoni sħiħa jirriżulta fil-formazzjoni ta' aktar karburi primarji. Dawn il-partiċelli ma jinħallux waqt it-ttemprar tas-soluzzjoni (1,050-1,100 grad) u jinżammu fit-tubi finali. F'soluzzjonijiet ta 'klorur dawn il-karburi preferibbilment jieħdu sehem fir-reazzjoni ta' tnaqqis ta 'ossiġnu katodiku u jiffurmaw par galvaniku li jiffavorixxi x-xoljiment anodiku tal-matriċi tal-madwar. Id-densità tal-bidu tal-fossa hija proporzjonali għan-numru tal-partiċelli primarji tal-karbur MC esposti fil-wiċċ.

Korrelazzjoni bejn Nijobju Eċċess, Frazzjoni tal-Volum MC u Prestazzjoni tal-Pitting

Testijiet ta' immersjoni kkontrollati b'347 tubi b'diversi livelli ta' nijobju (karbonju kostanti 0.05-0.06%, titanju<0.01%) in 1,000 ppm Cl- water (pH 7.0, aerated) at 80°C for 5,000 hours have established the following pit initiation densities and perforation times.

Nijobju (wt%) Nb:C Proporzjon Karbonju (wt%)MC Frazzjoni Volumetrika Primarja (%)MC Daqs tal-Partiċelli (µm) Densità tal-Fossa wara 5,000h (fosos/cm2) Fond Massimu tal-Ħofra wara 5,000h (µm) Ħin għall-Perforazzjoni (ħajt ta’ 1.5 mm, snin) Rakkomandat għal 81,{0} Grad ta’ Servizz 81,{0} 0.20 4:1 0.05 0.02-0.03 1-2 0.2-0.5 15-25 10-15 Aċċettabbli (taħt-stabbilizzat, periklu ta' sensitizzazzjoni)
0.30 6:1 0.05 0.03-0.04 1-2 0.3-0.6 18-28 9-12 Aċċettabbli 0.35 7:1 0.05 0.04-0.05 1-2 0.5-1.0 20-35 8-11 Aċċettabbli 0.40 8:1 0.05 0.05-0.06 1-3 0.8-1.5 25-40 6-9 Aċċettabbli (bilanċ ottimali) 0.45 9:1 0.05 0.06-0.08 2-4 1-2 30-50 5-7 Marġinali 0.50 10:{1 0.05 0.08-0.10 2-5 2-3 40-60 4-5 Mhux irrakkomandat 0.60 12:1 0.05 0.12-0.15 3-6 4-8 50-80 2.5-4 Le 0.70 14}}}:{13}} Le 0.70 14}}:{1} Le 1.00 20:1 0.05 0.25-0.30 6-12 25-40 100-150 0.8-1.2 Le
Influwenza tat-Temperatura tat-Ttemprar tas-Soluzzjoni fuq ix-Xoljiment Primarju tal-MC

It-temperaturi ogħla ta 'l-ittemprar tas-soluzzjoni jistgħu jdubu parzjalment il-karburi MC primarji, madankollu hemm riskju ta' qamħirrum li jgħaqqad u formazzjoni ta 'ferrite aktar minn 1,150 grad.

Temperatura tat-Ttemprar tas-Soluzzjoni (grad) Frazzjoni tal-Volum MC Primarja f'0.60% Nb (%) Daqs tal-Partiċelli MC (µm) Densità tal-Ħofra (fosos/cm2) Rakkomandat 1,050 0.12-0.15 3-6 4-8 Nru 1,080 0.10-0.12 3-5 3-6 Nru 1,100 0.08-0.10 3-4 2-4 Marġinali 1,120 0.06-0.08 2-4 1-3 Aċċettabbli ta' tkabbir tal-qamħ)
1,150 0.05-0.07 2-3 1-2 Aċċettabbli (grassing tal-qamħ → qawwa ta' creep aktar baxxa)
347 Rakkomandazzjonijiet Prattiċi għas-Servizz tal-Klorur

Ħajja ta' Servizz Mixtieqa (snin) Nijobju Massimu (wt%) Temperatura minima ta' Ttremprar tas-Soluzzjoni (oC) MC Primarju Massimu Vol. Frazzjoni (%) Stabbilizzazzjoni Suġġerita10 0.40 1,050 0.06 Xejn (anneal tas-soluzzjoni)
8-10 0.42 1,060 0.07 Xejn 5-8 0.45 1,080 0.08 Xejn (Evita l-istabbilizzazzjoni)
3-5 0.50 1,100 (b'aġġustament tad-daqs tal-qamħ) 0.10 Marġinali<3 >0.50Not recommended >0.10 Aġġorna għal 316L jew duplex 2205 Primary MC Carbide Content Verifika

Għall-konsumaturi li jeħtieġu xi reżistenza għall-pitting hemm żewġ modi biex tivverifika. L-ewwel hija spezzjoni metallografika SEM ta 'sezzjoni trasversali illustrata u kemmxejn inċiżi. Għadd il-karburi MC primarji (angolari, 2–10 µm) f'1,000× Aċċettazzjoni:<5 particles/mm2 for >Ħajja ta '8 snin